Castable 60
Castable 60 is a versatile high-alumina refractory castable, formulated for excellent performance in high-temperature applications up to 1600°C. With 60% alumina content, it offers a good balance between thermal resistance and mechanical strength, making it suitable for furnaces, kilns, and other heating equipment. Its ease of installation and superior durability make it an ideal choice for both repair and new construction projects.
General Specifications :
| Product Type | Whytheat K |
|---|---|
| Nature Of Bond | Hydraulic |
| Installation | Vibrations Casting |
| General Properties | |
| Max.Service Temperature | 1600. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 10.6-11.8 |
| Chemical Analysis % | Typical Value |
| AI2o3 | 56 - 60 |
| Fe2o3 | 1.00 - 1.25 |
| Cao | 4.00 - 4.70 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.15 - 2.25 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 350 - 430 |
| After Heating At 1100. C/3 hrs | 180 - 280 |
| After Heating At 1550. C/3 hrs | 350 - 500 |
| % Retained On max. Size | 0 - 5 |
| Thermal Properties | |
| Refractoriness, Orton / .C | 0.018419489 |
| PLC% | |
| After Heating at 1100.C/3 hrs | -0.40 to + 0.20 |
| After Heating at 1550.C/3 hrs | -1.20 to 2.40 |
| Packaging | 25 kg bags |
| Storage Life | 6 months |
| Delivery State | Dry |
Castable 90
Castable 90, with its 90% alumina content, is designed for the most demanding high-temperature applications, capable of withstanding temperatures up to 1800°C. This high-alumina castable provides exceptional resistance to slag, chemical attack, and wear, making it perfect for use in blast furnaces, foundries, and other extreme environments. Its high strength and thermal stability ensure long-lasting performance under the toughest conditions.
| Product Type | Whytheat A |
|---|---|
| Nature Of Bond | Hydraulic |
| Installation | Vibrations Casting |
| General Properties | |
| Max.Service Temperature | 1700. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 8.10-10.0% |
| Chemical Analysis % | Typical Value |
| AI2o3 | 85 - 90 |
| Fe2o3 | 0.8 - 1.5 |
| Cao | 5.5 - 06.5 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.65 - 2.80 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 600 - 700 |
| After Heating At 1100. C/3 hrs | 300 - 400 |
| After Heating At 1550. C/3 hrs | 650 - 800 |
| % Retained On max. Size | 0 - 5 |
| Thermal Properties | |
| Refractoriness, Orton / .C | 0.02032967 |
| PLC% | |
| after heating at 1100.C/3 hrs | -0.40 to + 0.20 |
| after heating at 1550.C/3 hrs | -1.00 to 2.50 |
| packaging | 25 kg bags |
| storage life | 6 months |
| delivery state | dry |